J.B. Li, Hui Yang, L.X. Zheng, D.P. Xu, Y.T. Wang
National Research Center for Opto-electronic Technology, Institute of Semiconductors
This article was presented as part of Symposium G, "Gallium Nitride and Related Alloys" at the 1998 Fall Meeting of the Materials Research Society held in Boston, Massachusetts, November 30-December 4.
We report on the growth of high-quality cubic phase InGaN on GaAs by MOCVD. The cubic InGaN layers are grown on cubic GaN buffer layers on GaAs (001) substrates. The surface morphology of the films are mirror-like. The cubic nature of the InGaN films is obtained by X-ray diffraction (XRD) measurements. The InGaN layers show strong photoluminescence (PL) at room temperature. Neither emission peak from wurtzite GaN nor yellow luminescence is observed in our films. The highest In content as determined by XRD is about 17% with an PL emission wavelength of 450 nm. The FWHM of the cubic InGaN PL peak are 153 meV and 216 meV for 427 nm and 450 nm emissions, respectively. It is found that the In compositions determined from XRD are not in agreement with those estimated from PL measurements. The reasons for this disagreement are discussed.
Full text of this article is available.
For information about using Adobe Acrobat files, click here .
Cite this article as: MRS Internet J. Nitride Semicond. Res. 4S1, G3.25 (1999).
|
|
|
Reference List Building For information on building reference lists, see About the MIJ-NSR Reference List Builder |